Korean Journal of Metals and Materials 2016;54(9): 659-671. doi: https://doi.org/10.3365/KJMM.2016.54.9.659
1Cr-1.25Mo-0.25V 강 잉곳의 응고편석 및 균질화 거동
김동배1,3, 나영상2, 서성문2, 이재현3
2한국기계연구원 부설 재료연구소
3창원대학교 나노신소재공학과
Solidification Segregation and Homogenization Behavior of 1Cr-1.25Mo-0.25V Steel Ingot
Dong-Bae Kim1,3, Young-Sang Na2, Seong-Moon Seo2, Je-Hyun Lee3
1Dae-gu Mechatronics & Materials Institute, Daegu 42714, Republic of Korea
2Korea Institute of Materials Science, Gyeongnam 51508, Republic of Korea
3Changwon National University, Department of Metallurgy & Materials Engineering, Gyeongnam 51140, Republic of Korea
Correspondence  Young-Sang Na ,Tel: +82-55-280-3377, Email: nys1664@kims.re.kr
Received: 18 November 2015;  Accepted: 17 March 2016.  Published online: 5 September 2016.
As a first step to optimizing the homogenization heat treatment following high temperature upset forging, the solidification segregation and the homogenization behaviors of solute elements were quantitatively analyzed for 1Cr-1.25Mo-0.25V steel ingot by electron probe micro-analysis (EPMA). The random sampling approach, which was designed to generate continuous compositional profiles of each solute element, was employed to clarify the segregation and homogenization behaviors. In addition, ingot castings of lab-scale and a 16-ton-sized 1Cr-1.25Mo-0.25V steel were simulated using the finite element method in three dimensions to understand the size effect of the ingot on the microsegregation and its reduction during the homogenization heat treatment. It was found that the microsegregation in a large-sized ingot was significantly reduced by the promotion of solid state diffusion due to the extremely low cooling rate. On the other hand, from the homogenization point of view, increasing the ingot size causes a dramatic increase in the dendrite arm spacing, and hence the homogenization of microsegregation in a large-sized ingot appears to be practically difficult.
Keywords: 1Cr-1.25Mo-0.25V steel, solidification segregation, homogenization, secondary dendrite arm spacing, residual segregation index
PDF Links  PDF Links
Full text via DOI  Full text via DOI
Download Citation  Download Citation
Related article
Editorial Office
The Korean Institute of Metals and Materials
6th Fl., Seocho-daero 56-gil 38, Seocho-gu, Seoul 06633, Korea
TEL: +82-2-557-1071   FAX: +82-2-557-1080   E-mail: metal@kim.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Institute of Metals and Materials.                 Developed in M2PI