Abstract
Single-crystal superalloys have been popularly employed in high-temperature parts of gas turbines, such as blades. However, the welds of such alloys are highly susceptible to solidification cracking, which limits their applicability to high-temperature turbine blades. In this study, the effects of characteristics of weld solidification on solidification cracking susceptibilities (solidification..... More

Abstract
In this study, the relationship between solidification cracking and epitaxial growth behavior with the high-speed laser surface melting of a directionally solidified 247LC superalloys was fundamentally and metallurgically investigated, to develop a successful welding procedure for the next generation of gas turbine blades. Under typical laser surface melting conditions (scan..... More

Abstract
The metallurgical aspects of weld solidification cracking in Ni-based superalloys (with Ti+Al > 5 mass%) have not been widely investigated thus far. Herein, the solidification cracking susceptibility of the CM247LC superalloy and its welds with ERNiFeCr-2 filler wire was quantitatively evaluated using a novel modified Varestraint testing method, for the..... More

Abstract
The metallurgical aspects of weld cracking in Ni-based superalloys remain relatively unexplored in existing research. The present study performed comprehensive metallurgical and manufactural investigations into the weldability of an Ni-based superalloy, CM247LC, from the viewpoint of the liquation cracking behavior and its susceptibility. Metallurgical solutions to suppress the liquation-cracking susceptibility..... More

Abstract
In this study, the weldability of the as-cast CM247LC superalloy for turbine blade applications was metallurgically evaluated in terms of its hot cracking behavior and susceptibility. For this purpose, a real blade was manufactured using a directional solidification casting process, and gas tungsten arc welding was performed at the tip..... More

Abstract
Investment casting for the thin (4 mm thick) rectangular tube (40 mm wide, 80 mm high and 200 mm long) was carried out numerically and experimentally for Alloy 738, which is a precipitation-hardened Ni-base superalloy. Two types of rectangular tubes, one with a regular array (10 mm by 10 mm..... More