Abstract
The effect of solution temperature and quench delay on the microstructure and mechanical properties of an extruded Al-Mg-Si-Cu-Mn alloy was investigated by employing differential scanning calorimetry, transmission electron microscopy, hardness test, and tensile test. The extruded specimens were held at 500 and 540 ^oC, respectively, for 80 min for solutionizing..... More

Abstract
An ultrasonic nanocrystal surface modification (UNSM) technique was applied to a 1-mm thick AZ31 magnesium sheet. UNSM is a relatively new surface modification technique in which a hard, hemispherical tip (2.38 mm in diameter) strikes the surface at an ultrasonic frequency to induce plastically deformed gradient microstructures and deep compressive..... More

Abstract
The effects of the cooling rate, after solution heat treatment, on the microstructures and mechanical properties of Fe-22Mn-8Al-0.8C-0.02Nb (low carbon) and Fe-20Mn-8Al-1.1C-0.1Nb (high carbon) light-weight steels were systematically investigated. The cooling process was controlled to achieve six different cooling rates, ranging from -0.016 to -465.1 ^oC/s. Under the slowest cooling..... More

Abstract
The effects of heat treatment conditions on the mechanical properties and energy absorption capacity of 7003 (Al-6Zn-0.6Mg) aluminum alloy were studied. The extruded material was heat treated at various temperatures to prepare annealed or aged specimens. Tensile tests, hardness measurements, electron backscatter diffraction characterizations, and differential scanning calorimeter analyses were..... More

Abstract
Investment casting for the thin (4 mm thick) rectangular tube (40 mm wide, 80 mm high and 200 mm long) was carried out numerically and experimentally for Alloy 738, which is a precipitation-hardened Ni-base superalloy. Two types of rectangular tubes, one with a regular array (10 mm by 10 mm..... More